Increasing global production of Portland cement and the need to reduce CO2
emissions create the need to increase the production of blended cement. Recently,
calcined clays are very promising for this need. In this study, the behavior of micro
concrete under high temperature produced with blended cement containing calcined
marl was investigated. It was used 4 different mixtures for micro concretes produced
with blended cements containing calcined marl at 0%, 10%, 20% and 30% replacement
ratios. In the study, saturated and dry density, water absorption ratios, ultra pulse
velocities, weight losses, flexural-compressive strengths of micro concretes were
determined. Temperatures of 300°C, 600°C and 800°C were used to determine the
behavior of micro-concrete under high temperature. The flexural-compressive
strengths of micro-concrete containing alternative pozzolan calcined marl blended
cements are improved up to 20% replacement. It has been determined that calcined
marl additive has positive effects on the fire resistance of micro concretes under the
effect of high temperature.,Portland çimentosunun artan küresel üretimi ve CO2 emisyonlarını azaltma
gerekliliği katkılı çimentoların üretimini artırma ihtiyacını oluşturmaktadır. Son
zamanlarda, kalsine killer, bu ihtiyaca yönelik olarak oldukça umut vericidir. Bu
çalışmada, kalsine marn katkılı mikro betonların yüksek sıcaklık etkisindeki
davranışları incelenmiştir. %0, %10, %20 ve %30 yer değiştirme yüzdelerinde kalsine
marn içeren katkılı çimentolarla üretilen mikro betonlar için 4 farklı karışım
kullanılmıştır. Çalışmada, mikro betonların doygun kuru yüzeyli ve kuru birim
ağırlıkları ile su emme oranları, utrases geçiş hızları, ağırlık kayıpları, eğilme-basınç
dayanımları belirlenmiştir. Mikro betonların yüksek sıcaklık etkisindeki davranışların
belirlenmesi amacıyla, 300°C, 600°C ve 800 °C sıcaklıklar kullanılmıştır.
Alternatif puzolan kalsine marn katkılı çimentolar içeren mikro betonların eğilmebasınç dayanımları %20 yer değiştirme miktarına kadar artmıştır. Kalsine marn katkısı
yüksek sıcaklık etkisi altında mikro betonların yangın dayanımına olumlu etkileri
olduğu tespit edilmiştir.
Increasing global production of Portland cement and the need to reduce CO2
emissions create the need to increase the production of blended cement. Recently,
calcined clays are very promising for this need. In this study, the behavior of micro
concrete under high temperature produced with blended cement containing calcined
marl was investigated. It was used 4 different mixtures for micro concretes produced
with blended cements containing calcined marl at 0%, 10%, 20% and 30% replacement
ratios. In the study, saturated and dry density, water absorption ratios, ultra pulse
velocities, weight losses, flexural-compressive strengths of micro concretes were
determined. Temperatures of 300°C, 600°C and 800°C were used to determine the
behavior of micro-concrete under high temperature. The flexural-compressive
strengths of micro-concrete containing alternative pozzolan calcined marl blended
cements are improved up to 20% replacement. It has been determined that calcined
marl additive has positive effects on the fire resistance of micro concretes under the
effect of high temperature.,Portland çimentosunun artan küresel üretimi ve CO2 emisyonlarını azaltma
gerekliliği katkılı çimentoların üretimini artırma ihtiyacını oluşturmaktadır. Son
zamanlarda, kalsine killer, bu ihtiyaca yönelik olarak oldukça umut vericidir. Bu
çalışmada, kalsine marn katkılı mikro betonların yüksek sıcaklık etkisindeki
davranışları incelenmiştir. %0, %10, %20 ve %30 yer değiştirme yüzdelerinde kalsine
marn içeren katkılı çimentolarla üretilen mikro betonlar için 4 farklı karışım
kullanılmıştır. Çalışmada, mikro betonların doygun kuru yüzeyli ve kuru birim
ağırlıkları ile su emme oranları, utrases geçiş hızları, ağırlık kayıpları, eğilme-basınç
dayanımları belirlenmiştir. Mikro betonların yüksek sıcaklık etkisindeki davranışların
belirlenmesi amacıyla, 300°C, 600°C ve 800 °C sıcaklıklar kullanılmıştır.
Alternatif puzolan kalsine marn katkılı çimentolar içeren mikro betonların eğilmebasınç dayanımları %20 yer değiştirme miktarına kadar artmıştır. Kalsine marn katkısı
yüksek sıcaklık etkisi altında mikro betonların yangın dayanımına olumlu etkileri
olduğu tespit edilmiştir.